Special Release Film
Jul 01, 2026
On-line coating matte release film / MMR
Product Description:
On-line coating matte release film / MMR, is evenly coated with emulsion silicon release agent on the surface of matte film, which can be used in car clothing and color modification film protection, etc.
Feature:
Online coating process production, uniform coating
▲Stable release force, high subsequent adhesion
▲Good surface flatness . No risk of contamination caused by
secondary processing
Typical Properties:
| Properties | Test methods | Units | Typical Value | ||
| Thickness | GB/T 6672 | μm | 45 | 70 | |
| Tensile Strength | MD | ASTM D882 | MPa | 150 | |
| TD | ASTM D882 | MPa | 220 | ||
| Heat Shrinkage | MD | ASTM D1204 150℃/30min | % | 1.0 | |
| TD | ASTM D1204 150℃/30min | % | 0 | ||
| Haze | ASTM D1003 | % | 85 | 95 | |
| Transmission | ASTM D1003 | % | 80 | 78 | |
| Release force | Tesa 7475 Tape 30cm/min, 180° | g/inch | 20~40 | 30~60 | |
| Subsequent adhesion | Nitto 31B Tape | % | 90 | 90 | |
Advantages:
Better coating uniformity
More consistent release force
Excellent surface flatness
Reduced coating defects
Improved cleanliness
Higher production efficiency
Because the coating becomes an integral part of the film production process, the final product typically demonstrates better quality consistency than conventional off-line coated films.
Application
Laser imprinting film
Product Description:
Laser imprinting film / LS is widely used for packaging various types of luxury paper boxes and film bags. Laser patterns can be directly
moulded on PET film to make the packaging environmentally friendly and aesthetically pleasing.
Product Feature:
▲Low temperature molding
▲The information in the layer is completed and high brightness
▲Excellent dimensional stability and temperature resistance
Product Structure
Product picture
product key technologies
Embossed laser patterns create dynamic holographic effects that change with viewing angles, helping products stand out on retail shelves.
The film performs well during lamination, slitting, die cutting, embossing, and printing processes, making it suitable for automated converting lines.
Product Application:
Laser Imprinting Film is widely used in decorative packaging and premium printing applications, including:
- Luxury paper boxes
- Cosmetic packaging
- Perfume boxes
- Gift boxes
- Wine and liquor packaging
- Shopping bags
- Greeting cards
- Premium labels and stickers
- Book covers
- Tobacco packaging
- Food packaging decoration
- Promotional packaging
- Laminated paper products
- Decorative PET films
Application picture
Typical Properties
| Properties | Test methods | Unit | Typical Value | ||
| Thickness | GB/T 6672 | µm | 13 | 50 | |
| Tensile Strength | MD | ASTM D882 | MPa | 190 | 180 |
| TD | 210 | 210 | |||
| Heat Shrinkage | MD | ASTM D1204 150℃/ 30min |
% | 1.5 | |
| TD | -0.1 | ||||
| Coefficient of Friction | µs | GB/T 10006 | - | 0.400 | |
| µd | 0.380 | ||||
| Gloss 45° | ASTM D2457 | % | 115.0 | ||
| Haze | ASTM D1003 | % | 2.0 | 2.5 | |
| Surface Wetting Tension | Corona treated | GB/T 14216 | mN/m | 56 | |
| Untreated | 40 | ||||
On-line coating matte release film / MLR
Product Description:
On-line coating matte release film / MLR, is evenly coated with emulsion silicon release agent on the surface of matte film, which can be used in tape processing, adhesive release protection, etc.
Product Structure
Product Feature
Online coating process production, uniform coating
Stable release force, high subsequent adhesion
Typical Properties
| Properties | Test methods | Units | Typical Values | |||
| Thickness | GB/T 6672 | μm | 15 | 25 | ||
| Tensile Strength |
MD | ASTM D882 | MPa | 150 | ||
| TD | 220 | |||||
| Heat Shrinkage | MD | ASTM D1204 150℃/30min | % | 1.5 | ||
| TD | 0 | |||||
| Haze | ASTM D1003 | % | 45 | 50 | ||
| Transmission | ASTM D1003 | % | 88 | 88 | ||
| Release force | Tesa 7475 Tape 30cm/min, 180° | g/inch | 15 | 15 | ||
| Subsequent adhesion | Nitto 31B Tape | % | 92 | 92 | ||